Título : Estudio comparativo de microfiltración coronal utilizando dos cementos de obturación temporal, en dientes endodonciados
Autor: Tobar Guaranda, Johanna Del Carmen
Palabras clave : MICROFILTRACION;ENDODONCIA;CAVIT
Fecha de publicación : may-2016
Abstract: El propósito de la presente investigación es evaluar in vitro la microfiltración coronal comparando dos materiales de obturación temporal: Coltosol y CAVİT 3M en piezas uniradiculares en dientes endodonciados, el objetivo es evaluar la incidencia de la presencia de microfiltraciones en obturación temporal, utilizando los cementos dentales cavit, coltosol. Se realizo un estudio comparativo de microfiltración Coronal utilizando dos cementos de obturación temporal, en dientes endodonciados, realizamos un estudio in vitrio donde se seleccionaron 26 premolares humanos uniradiculares con rizogénesis completa y sin tratamiento endodóntico previo. Los dientes fueron almacenados en hipoclorito, luego se los coloco en suero fisiológico para mantenerlos hidratados. Todos los dientes fueron preparados con la técnica apico-coronal. Fueron preparados con instrumentos tipo k irrigados con hipoclorito de sodio en una concentración de 2,5%. Posteriormente los dientes fueron obturados, utilizando el cemento obturador SELAPEX , Se colocó una capa de 1mm de Ionomero de Vitrio de fotocurado previo a la colocación del cemento de obturación temporal Las piezas dentarias del G1 se les coloco 3mm de Coltosol a nivel cameral como cemento de obturación temporal se esperó 48 horas, para su endurecimiento total. Como conclusiones tenemos que el grupo de dientes que tiene mayor frecuencia de microfiltración coronal son los dientes que se utilizó COLTOSOL, bajo las condiciones de este estudio se concluye que las obturaciones con coltosol presentaron menor microfiltración coronal, en grados y milímetros, que las obturaciones de cavit 3m como cemento provisional, se comprobó Las propiedades de biocompatibilidad, y gran adhesión, que tiene el coltosol.
The purpose of this research is to evaluate in vitro the coronal microleakage comparing two materials, temporary filling: Coltosol and Cavit 3M uniradiculares pieces in endodontic teeth, the objective is to assess the impact of the presence of microleakage in temporary filling, using dental cements Cavit, Coltosol. A comparative study of Coronal microfiltration using two temporary filling cements in endodontic teeth was performed, we conducted a study in which 26 uniradiculares vitrio human premolars were selected with complete rizogénesis and without endodontic treatment. The teeth were stored in hypochlorite, then they placed them in saline to keep them hydrated. All teeth were prepared with apico-coronal technique. They were prepared with type k instruments irrigated with sodium hypochlorite at a concentration of 2.5%. Subsequently the teeth were sealed using the sealing cement SELAPEX a 1mm layer ionomer Vitrio prior to placing cement temporary filling the teeth of G1 fotocurado was placed were placed 3mm Coltosol to cameral level cement temporary sealing waited 48 hours for full curing. As conclusions we have the group of teeth that have higher frequency of coronal microfiltration are the teeth Coltosol used under the conditions of this study is concluded that the seals with Coltosol had lower coronal microfiltration, in degrees and millimeters, fillings Cavit 3m as temporary cement, biocompatibility properties was found, and high adhesion, which has the Coltosol.
Resumen : pdf
URI : http://repositorio.ug.edu.ec/handle/redug/13900
Aparece en las colecciones: Tesinas - Odontología

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Johanna Tobar G.pdfBODONT23491,01 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.